By an in-situ seeding synthetic route, with biocompatible reagents being used, walnut kernel-like Ag nanostructures (Ag nanowalnuts) composed of nanoplates were fabricated. The in-situ formation of seeds and introduction of complex [Ag3(C6H5O7)n+1]3n−were indispensable steps for this kind of self-assembled nanostructure. The size of Ag nanowalnuts was in the range of 200–400 nm and the thickness of a single nanoplate was about 30 nm. The morphology of nanoplates was of variety, and their surface was bumpy. Such Ag nanostructures with rough surface and high curvature provided plenty of ‘hot spots’ on a single particle for surface-enhanced Raman scattering (SERS) enhancement. Experimental results indicated that the Ag nanowalnuts offered great surface enhancement for 4-mercaptobenzoic acid and malachite green molecules. The limit of detection was low to 10−10 and 10−8 M, respectively.
References
-
-
1)
-
38. Jin, R., Cao, Y.C., Hao, E., et al: ‘Controlling anisotropic nanoparticle growth through plasmon excitation’, Nature, 2003, 425, (6957), pp. 487–490 (doi: 10.1038/nature02020).
-
2)
-
19. Sun, Y.F., Wang, L.W., Liu, J.H., et al: ‘Tunable surface plasma resonance of gold nanorods superstructure and their SERS properties’, Micro Nano Lett., 2018, 13, pp. 1265–1268 (doi: 10.1049/mnl.2018.5103).
-
3)
-
3. Yang, D., Zhou, Q., Zhang, L.S., et al: ‘Preparation of silver fractal nanostructures and their application in surface enhanced Raman scattering’, Mater. Lett., 2020, 258, pp. 126808–126810 (doi: 10.1016/j.matlet.2019.126808).
-
4)
-
20. Gu, G.H., Suh, J.S.: ‘Silver nanorods used to promote SERS as a quantitative analytical tool’, J. Raman Spectrosc., 2010, 41, pp. 624–627 (doi: 10.1002/jrs.2487).
-
5)
-
2. Cao, Y.C., Jin, R., Mirkin, C.A., et al: ‘Nanoparticales with Raman spectroscopic fingerprints for DNA and RNA detection’, Science, 2002, 297, pp. 1536–1540 (doi: 10.1126/science.297.5586.1536).
-
6)
-
15. Si, G.L., Shi, W.T., Li, K., et al: ‘Synthesis of PSS-capped triangular silver nanoplates with tunable SPR’, Colloids Surf., A, Physicochem. Eng. Aspects, 2011, 380, pp. 257–260 (doi: 10.1016/j.colsurfa.2011.02.023).
-
7)
-
18. He, L.L., Kim, N.J., Li, H., et al: ‘Use of a fractal-like gold nanostructure in surface-enhanced Raman spectroscopy for detection of selected food contaminants’, J. Agric. Food Chem., 2008, 56, pp. 9843–9847 (doi: 10.1021/jf801969v).
-
8)
-
10. Zhang, C.Y., Hao, R., Zhao, B., et al: ‘Graphene oxide-wrapped flower-like sliver particles for surface-enhanced Raman spectroscopy and their applications in polychlorinated biphenyls detection’, Appl. Surf. Sci., 2017, 400, pp. 49–56 (doi: 10.1016/j.apsusc.2016.12.161).
-
9)
-
6. Giannini, V., Rodríguez-Oliveros, R., Sánchez-Gil, J.A., et al: ‘Surface plasmon resonances of metallic nanostars/nanoflowers for surface-enhanced Raman scattering’, Plasmonics., 2010, 5, pp. 99–104 (doi: 10.1007/s11468-009-9121-3).
-
10)
-
1. Chen, Y., Fan, Z., Zhang, Z., et al: ‘Two-dimensional metal nanomaterials: synthesis, properties, and applications’, Chem. Rev., 2018, 118, pp. 6409–6455 (doi: 10.1021/acs.chemrev.7b00727).
-
11)
-
4. Yüksel, S., Ziegler, M., Goerke, S., et al: ‘Hierarchically-designed 3D flower-like composite nanostructures as an ultrastable, reproducible, and sensitive SERS substrate’, ACS Appl. Mater. Interfaces, 2017, 9, pp. 38854–38862 (doi: 10.1021/acsami.7b14833).
-
12)
-
8. Xia, Y., Gao, Z.N., Liao, X.M., et al: ‘Rapid synthesis of hierarchical, flower-like Ag microstructures with a gemini surfactant as a directing agent for SERS applications’, CrystEngComm, 2017, 19, pp. 6547–6555 (doi: 10.1039/C7CE01573A).
-
13)
-
28. Kelly, K.L., Coronado, E., Zhao, L.L., et al: ‘The optical properties of metal nanoparticles: the influence of size, shape, and dielectric environment’, Phys. Chem. B., 2003, (107), pp. 668–677 (doi: 10.1021/jp026731y).
-
14)
-
9. Chiu, C.W., Lin, P.H.: ‘Hierarchical self-assembly of random mica nanosheet-stabilized silver nanoparticles into flower microstructures for highly sensitive SERS substrates’, RSC Adv., 2015, 5, pp. 86522–86528 (doi: 10.1039/C5RA16872D).
-
15)
-
7. Liang, H., Li, Z., Wang, W., et al: ‘Highly surface-roughened ‘flower-like’ silver nanoparticles for extremely sensitive substrates of surface-enhanced Raman scattering’, Adv. Mater., 2009, 21, pp. 4614–4618 (doi: 10.1002/adma.200901139).
-
16)
-
21. Darienzo, R.E., Chen, O., Sullivan, M., et al: ‘Au nanoparticles for SERS: temperature-controlled nanoparticle morphologies and their Raman enhancing properties’, Mater. Chem. Phys., 2020, 240, pp. 122143–122152 (doi: 10.1016/j.matchemphys.2019.122143).
-
17)
-
5. Garcia-Leis, A., Rivera-Arreba, I., Sanchez-Cortes, S., et al: ‘Morphological tuning of plasmonic silver nanostars by controlling the nanoparticle growth mechanism: application in the SERS detection of the amyloid marker Congo Red’, Colloids Surf. A, Physicochem. Eng. Aspects, 2017, 535, pp. 49–60 (doi: 10.1016/j.colsurfa.2017.09.013).
-
18)
-
16. Teguh, J.S., Liu, F., Xing, B., et al: ‘Surface-enhanced Raman scattering (SERS) of nitrothiophenol isomers chemisorbed on TiO2’, Chem.-Asian J., 2012, 7, pp. 975–981 (doi: 10.1002/asia.201100934).
-
19)
-
17. Jiang, L., You, T.T., Yin, P.G., et al: ‘Surface-enhanced Raman scattering spectra of adsorbates on Cu2O nanospheres: charge-transfer and electromagnetic enhancement’, Nanoscale, 2013, 5, pp. 2784–2789 (doi: 10.1039/c3nr33502j).
-
20)
-
12. Jin, R.C., Cao, Y.W., Mirkin, C.A., et al: ‘Photoinduced conversion of silver nanospheres to nanoprisms’, Science, 2001, 294, pp. 1901–1903 (doi: 10.1126/science.1066541).
-
21)
-
11. Jiang, X.C., Chen, C.Y., Chen, W.M., et al: ‘Role of citric acid in the formation of silver nanoplates through a synergistic reduction approach’, Langmuir, 2010, 26, pp. 4400–4408 (doi: 10.1021/la903470f).
http://iet.metastore.ingenta.com/content/journals/10.1049/mnl.2020.0131
Related content
content/journals/10.1049/mnl.2020.0131
pub_keyword,iet_inspecKeyword,pub_concept
6
6