The authors have synthesised a kind of low shrinkage alumina (Al2O3) aerogel using an inexpensive salt of aluminium (AlCl3·6H2O) via tetraethoxysilane modification and an ambient pressure drying process. The morphology, pore structure, surface group, crystal phase and thermal properties of the Al2O3 aerogel are analysed by X-ray diffractometer, scanning electron microscopy, Fourier transform infrared spectra and nitrogen adsorption test. Further improvement in thermal stability and thermal shrinkage are obtained by incorporation of silicon (Si) atoms during the aerogel preparation. The specific surface area of modified aerogel is 480 m2/g and the diameter shrinkage is 8% after drying, and reach 304 m2/g and 16.5% after heating at 1000°C. The approach, which is straightforward, inexpensive and safe, can be employed to prepare a monolithic mesoporous material with low shrinkage and high-temperature resistance. This will further promote the potential application of packaging and thermal insulation materials.
References
-
-
1)
-
11. Leventis, N., Sotiriouleventis, C., Guohui Zhang, A., et al: ‘Nanoengineering strong silica aerogels’, Nano Lett., 2002, 2, pp. 957–960 (doi: 10.1021/nl025690e).
-
2)
-
16. Ji, L., Lin, J., Tan, K.L., et al: ‘Synthesis of high-surface-area alumina using aluminum tri-sec-butoxide-2,4-pentanedione-2-propanol-nitric acid precursors’, Chem. Mater., 2000, 12, pp. 931–939 (doi: 10.1021/cm990404u).
-
3)
-
24. Wang, W., Zhang, Z., Zu, G., et al: ‘Trimethylethoxysilane-modified super heat resistant alumina aerogels for high-temperature thermal insulation and adsorption applications’, RSC Adv., 2014, 4, (97), pp. 54864–54871 (doi: 10.1039/C4RA08832H).
-
4)
-
3. Hrubesh, L.W.: ‘Aerogel applications’, J. Non-Cryst. Solids, 1998, 225, pp. 335–342 (doi: 10.1016/S0022-3093(98)00135-5).
-
5)
-
10. Wang, Y., Zou, Y., Chen, J., et al: ‘A flexible and monolithic nanocomposite aerogel of carbon nanofibers and crystalline titania: fabrication and applications’, RSC Adv., 2013, 3, pp. 24163–24168 (doi: 10.1039/c3ra44820g).
-
6)
-
8. Hilonga, A., Kim, J.-K., Sarawade, P.B., et al: ‘Low-density TEOS-based silica aerogels prepared at ambient pressure using isopropanol as the preparative solvent’, J. Alloys Compd.., 2009, 487, pp. 744–750 (doi: 10.1016/j.jallcom.2009.08.055).
-
7)
-
19. Prakash, S.S., Brinker, C.J., Hurd, A.J., et al: ‘Erratum: silica aerogel films prepared at ambient pressure by using surface derivatization to induce reversible drying shrinkage’, Nature, 1995, 375, p. 431 (doi: 10.1038/375431b0).
-
8)
-
22. Wu, L., Huang, Y., Wang, Z., et al: ‘Fabrication of hydrophobic alumina aerogel monoliths by surface modification and ambient pressure drying’, Appl. Surf. Sci., 2010, 256, pp. 5973–5977 (doi: 10.1016/j.apsusc.2010.03.104).
-
9)
-
14. Zu, G., Shen, J., Wei, X., et al: ‘Preparation and characterization of monolithic alumina aerogels’, J. Non-Cryst. Solids, 2011, 357, pp. 2903–2906 (doi: 10.1016/j.jnoncrysol.2011.03.031).
-
10)
-
7. Xiao, L., Grogan, M.D.W., England, R., et al: ‘Stable low-loss optical nanofibres embedded in hydrophobic aerogel’, Opt. Express, 2011, 19, p. 764 (doi: 10.1364/OE.19.000764).
-
11)
-
1. Gurav, J.L., Jung, I.-K., Park, H.-H., et al: ‘Silica aerogel: synthesis and applications’, J. Nanomater., 2010, 2010, pp. 1–11 (doi: 10.1155/2010/409310).
-
12)
-
4. Pierre, A.C., Pajonk, G.M.: ‘Chemistry of aerogels and their applications’, ChemInform, 2002, 102, p. 4243.
-
13)
-
2. Yang, X., Wei, J., Shi, D., et al: ‘Comparative investigation of creep behavior of ceramic fiber-reinforced alumina and silica aerogel’, Mater. Sci. Eng. A, 2014, 609, pp. 125–130 (doi: 10.1016/j.msea.2014.04.099).
-
14)
-
23. Horiuchi, T., Osaki, T., Sugiyama, T., et al: ‘Maintenance of large surface area of alumina heated at elevated temperatures above 1300°C by preparing silica containing pseudo-boehmite aerogel’, J. Non-Cryst. Solids, 2001, 291, pp. 187–198 (doi: 10.1016/S0022-3093(01)00817-1).
-
15)
-
18. Carlson, G., Lewis, D., Mckinley, K., et al: ‘Aerogel commercialization: technology, markets and costs’, J. Non-Cryst. Solids, 1995, 186, pp. 372–379 (doi: 10.1016/0022-3093(95)00069-0).
-
16)
-
5. Al-Yassir, N., Le Van Mao, R.: ‘Thermal stability of alumina aerogel doped with yttrium oxide, used as a catalyst support for the thermocatalytic cracking (TCC) process: an investigation of its textural and structural properties’, Appl. Catal. A, Gen., 2007, 317, pp. 275–283 (doi: 10.1016/j.apcata.2006.10.030).
-
17)
-
17. Grader, G.S., Rifkin, Y., Cohen, Y., et al: ‘Preparation of alumina aerogel films by low temperature CO2 supercritical drying process’, J. Sol-Gel Sci. Technol., 1997, 8, pp. 825–829.
-
18)
-
20. Kocon, L., Despetis, F., Phalippou, J.: ‘Ultralow density silica aerogels by alcohol supercritical drying’, J. Non-Cryst. Solids, 1998, 225, pp. 96–100 (doi: 10.1016/S0022-3093(98)00322-6).
-
19)
-
12. Balakumar, K., Kalaiselvi, N.: ‘High sulfur loaded carbon aerogel cathode for lithium– sulfur batteries’, RSC Adv., 2015, 5, pp. 34008–34018 (doi: 10.1039/C5RA01436K).
-
20)
-
6. Smith, D.M., Maskara, A., Boes, U.: ‘Aerogel-based thermal insulation’, J. Non-Cryst. Solids, 1998, 225, pp. 254–259 (doi: 10.1016/S0022-3093(98)00125-2).
-
21)
-
15. Wu, X., Shao, G., Cui, S., et al: ‘Synthesis of a novel Al2O3–SiO2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum’, Ceram. Int., 2016, 42, pp. 874–882 (doi: 10.1016/j.ceramint.2015.09.012).
-
22)
-
13. Poco, J.F., Satcher, J.H.Jr., Hrubesh, L.W.: ‘Synthesis of high porosity, monolithic alumina aerogels’, J. Non-Cryst. Solids, 2001, 285, pp. 57–63 (doi: 10.1016/S0022-3093(01)00432-X).
-
23)
-
17. Baumann, T.F., Gash, A.E., Chinn, S.C., et al: ‘Synthesis of high-surface-area alumina aerogels without the use of alkoxide precursors’, Chem. Mater., 2005, 17, (2), pp. 395–401 (doi: 10.1021/cm048800m).
-
24)
-
9. Kistler, S.S.: ‘Coherent expanded aerogels and jellies’, Nature, 1931, 127, p. 741 (doi: 10.1038/127741a0).
http://iet.metastore.ingenta.com/content/journals/10.1049/mnl.2018.5077
Related content
content/journals/10.1049/mnl.2018.5077
pub_keyword,iet_inspecKeyword,pub_concept
6
6