Enhanced donor activities have been obtained after annealing at 700°C for selenium implants into GaAs by implanting an equal dose of gallium together with the selenium. Donor concentration depth profiles, measured for both single and dual implants of 1×1013/cm2 and 2×1014/cm2 indicated that the increase in activity was mainly due to an increase in peak donor concentration for the dual implants compared with those measured for single implants.
References
-
-
1)
-
A.G. Foyt ,
J.P. Donnelly ,
W.T. Lindley
.
Efficient doping of GaAs by Se+ ion implantation.
Appl. Phys. Lett.
,
372 -
374
-
2)
-
B.J. Sealy ,
R.K. Surridge
.
A new thin film encapsulant for ion implanted GaAs.
Thin Solid Films
,
L19 -
L22
-
3)
-
J.M. Woodcock ,
J.M. Shannon ,
D.J. Clark
.
Electrical and cathodoluminescence measurements on ion implanted donor layers in GaAs.
Solid State Electron
,
267 -
278
-
4)
-
Müller, H., Gyulai, J., Mayer, J.W., Eisen, F.H., Welch, B.: `Anodic oxidation and profile determination of ion implanted semi-insulating GaAs', Proceedings of conference on ion implantation, 1974, Osaka.
-
5)
-
T. Ambridge ,
R. Heckingbottom
.
Ion implantation in Compound semiconductors—an approach based on solid state theory.
Radiat. Eff.
,
31 -
36
-
6)
-
C.J. Hwang
.
Optical properties of n-type GaAs: II formation of efficient hole traps during annealing in Te-doped GaAs.
J. Appl. Phys.
,
4584 -
4590
-
7)
-
E.C. Bell ,
B.J. Sealy ,
R.K. Surridge
.
An electrical and RBS investigation of Si3N4 coatings on GaAs.
-
8)
-
J.S. Harris ,
F.H. Eisen ,
B. Welch ,
J.D. Haskell ,
R.D. Pashley ,
J.W. Mayer
.
Influence of implantation temperature and surface protection on tellurium implantation in GaAs.
Appl. Phys. Lett.
,
601 -
603
-
9)
-
Eisen, F.H., Harris, J.S., Welch, B., Pashley, R.D., Sigurd, D., Mayer, J.W.: `Properties of tellurium implanted GaAs', Conference on ion implantation in semiconductors and other materials, 1972, Yorktown Heights .
http://iet.metastore.ingenta.com/content/journals/10.1049/el_19750241
Related content
content/journals/10.1049/el_19750241
pub_keyword,iet_inspecKeyword,pub_concept
6
6