access icon free Al:ZnO top electrodes deposited with various oxygen pressures for ferroelectric (Pb,La)(Zr,Ti)O3 capacitors

Ferroelectric (Pb,La)(Zr,Ti)O3 capacitors were fabricated using chemical solution deposition with Al:ZnO (AZO) top electrodes that were deposited using pulsed laser deposition (PLD), where the oxygen pressure was varied systematically. The oxygen pressure during deposition of the AZO layer affected the surface morphology of the AZO top electrodes, as well as the ferroelectric properties of the capacitors. As the oxygen pressure increased, the AZO grains gradually appeared clearer in the SEM images, indicating less dense stacking, and the polarisation–voltage hysteresis loops expanded horizontally. The largest values of remnant polarisation and coercive voltage were obtained at 10 Pa. Appropriate ferroelectric properties were obtained for oxygen pressures in the range of 0.5–2.0 Pa. The hydrogen degradation resistance during annealing in 3% H2 200°C and 1 Torr was independent of oxygen pressure during PLD.

References

    1. 1)
    2. 2)
      • 7. Kim, H., Kim, J.-H., Choo, W.K.: ‘Preparation of conductive LaNiO3 thin films by using reactive RF magnetron sputtering with La and Ni metals’, J. Korean. Phys. Soc., 2003, 43, (5), pp. 847849, doi: 10.3938/jkps.43.847.
    3. 3)
    4. 4)
    5. 5)
    6. 6)
    7. 7)
    8. 8)
    9. 9)
    10. 10)
    11. 11)
      • 6. Guo, R., You, L., Zhou, Y., Lim, Z.S., Zou, X., Chen, L., Ramesh, R., Wang, J.: ‘Non-volatile memory based on the ferroelectric photovoltaic effect’, Nat. Commun., 2013, 4, p. 1990, doi: 10.1038/ncomms2990.
    12. 12)
    13. 13)
    14. 14)
    15. 15)
    16. 16)
http://iet.metastore.ingenta.com/content/journals/10.1049/el.2015.3539
Loading

Related content

content/journals/10.1049/el.2015.3539
pub_keyword,iet_inspecKeyword,pub_concept
6
6
Loading
Correspondence
This article has following corresponding article(s):
in brief
This is a required field
Please enter a valid email address