A simple method was used to produce a high concentration of single-layer graphene sheets in a single organic solvent system, without using any surfactants. In this experiment, the concentration of single-layer graphene sheets dispersed in solution increased as the sonication time increased, but damage occurred after performing sonication for 120 min. The concentration of single-layer graphene sheets was 0.915 mg/ml after sonication for 60 min. According to a transmission electron microscope image, the length of the single-layer graphene sheets was ∼2–3 μm, and the width was 0.5–1 μm. The perfect single-layer graphene sheets and the defective single-layer graphene sheets were distinguished using selected-area electron diffraction. X-ray diffraction determined that the two-theta angle of the numerous single-layer graphene sheets on a (002) plane was 25.57°, but the ‘one layer’ graphene sheets produced no peak along the (002) plane. According to the Raman spectra, the ratio of I_D /I_G was 0.3, which indicated that the graphene sheets contained few defects.

References

1. 1)
  - 8. Huang, X., Yin, Z.Y., Wu, S.X., et al: ‘Graphene-based materials: synthesis, characterization, properties, and applications’, Small, 2011, 7, pp. 1876–1902 (doi: 10.1002/smll.201002009).
2. 2)
  - A.A. Balandin , S. Ghosh , W.Z. Bao . Superior thermal conductivity of single-layer graphene. Nano Lett. , 902 - 907
3. 3)
  - 17. Hernandez, Y., Nicolosi, V., Lotya, M., et al: ‘High-yield production of graphene by liquid-phase exfoliation of graphite’, Nat. Nanotechnol., 2008, 3, pp. 563–568 (doi: 10.1038/nnano.2008.215).
4. 4)
  - 20. Tasis, D., Papagelis, K., Spiliopoulos, P., et al: ‘Efﬁcient exfoliation of graphene sheets in binary solvents’, Mater. Lett., 2013, 94, pp. 47–50 (doi: 10.1016/j.matlet.2012.12.027).
5. 5)
  - 4. Peigney, A., Laurent, C., Flahaut, E., et al: ‘Speciﬁc surface area of carbon nanotubes and bundles of carbon nanotubes’, Carbon, 2001, 39, pp. 507–514 (doi: 10.1016/S0008-6223(00)00155-X).
6. 6)
  - 5. Englert, J.M., Röhrl, J., Schmidt, C.D., et al: ‘Soluble graphene: generation of aqueous graphene solutions aided by a perylenebisimide-based bolaamphiphile’, Adv. Mater., 2009, 21, pp. 4265–4269 (doi: 10.1002/adma.200901578).
7. 7)
  - 10. Reina, A., Jia, X.T., Ho, J., et al: ‘Large area, few-layer graphene ﬁlms on arbitrary substrates by chemical vapor deposition’, Nano Lett., 2009, 9, pp. 30–35 (doi: 10.1021/nl801827v).
8. 8)
  - 14. Zhang, Y.B., Tang, T.T., Girit, C., et al: ‘Direct observation of a widely tunable bandgap in bilayer graphene’, Nature, 2009, 459, pp. 820–823 (doi: 10.1038/nature08105).
9. 9)
  - 15. Craciun, M.F., Russo, S., Yamamoto, M., et al: ‘Trilayer graphene is a semimetal with a gate-tunable band overlap’, Nat. Nanotechnol., 2009, 4, pp. 383–388 (doi: 10.1038/nnano.2009.89).
10. 10)
  - A.C. Ferrari , J.C. Meyer , V. Scardaci . Raman spectrum of graphene and graphene layers. Phys. Rev. Lett.
11. 11)
  - 9. Stankovich, S., Dikin, D.A., Piner, R.D., et al: ‘Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide’, Carbon, 2007, 45, pp. 1558–1565 (doi: 10.1016/j.carbon.2007.02.034).
12. 12)
  - K.S. Novoselov , A.K. Geim , S.V. Morozov , D. Jiang , Y. Zhang , S.V. Dubonos , I.V. Grigorieva , A.A. Firsov . Electric field effect in atomically thin carbon films. Science , 666 - 669
13. 13)
  - 18. Puangbuppha, B., Limsuwan, P., Asanithi, P.: ‘Non-chemically functionalized graphene exfoliated from graphite in water using ultrasonic treatment’, Proc. Eng., 2012, 32, pp. 1094–1099 (doi: 10.1016/j.proeng.2012.02.060).
14. 14)
  - 6. Mohanty, N., Berry, V.: ‘Graphene-based single bacterium resolution biodevice and DNA transistor: interfacing graphene derivatives with nanoscale and microscale biocomponents’, Nano Lett., 2008, 8, pp. 4469–4476 (doi: 10.1021/nl802412n).
15. 15)
  - 13. Ohta, T., Bostwick, A., Seyller, T., et al: ‘Controlling the electronic structure of bilayer graphene’, Science, 2006, 313, pp. 951–954 (doi: 10.1126/science.1130681).
16. 16)
  - 34. Meyer, J.C., Geim, A.K., Katsnelson, M.I., Novoselov, K.S., Booth, T.J., Roth, S.: ‘The structure of suspended graphene sheets’, Nature, 2007, 446, (7131), pp. 60–63 (doi: 10.1038/nature05545).
17. 17)
  - 16. Blake, P., Brimicombe, P.D., Nair, R.R., et al: ‘Graphene-based liquid crystal device’, Nano Lett., 2008, 8, pp. 1704–1708 (doi: 10.1021/nl080649i).
18. 18)
  - A.C. Ferrari , J. Robertson . Interpretation of Raman spectra of disordered and amorphous carbon. Phys. Rev. B , 14095 - 14107
19. 19)
  - 11. Hu, B., Ago, H., Ito, Y., et al: ‘Epitaxial growth of large-area single-layer graphene over Cu(111)/sapphire by atmospheric pressure CVD’, Carbon, 2012, 50, pp. 57–65 (doi: 10.1016/j.carbon.2011.08.002).
20. 20)
  - 7. Huang, X., Qi, X., Boey, F., et al: ‘Graphene-based composites’, Chem. Soc. Rev., 2012, 41, pp. 666–686 (doi: 10.1039/c1cs15078b).
21. 21)
  - 19. Sun, Z., Pöller, S., Huang, X., et al: ‘High-yield exfoliation of graphite in acrylate polymers: a stable few-layer graphene nanoﬂuid with enhanced thermal conductivity’, Carbon, 2013, 64, pp. 288–94 (doi: 10.1016/j.carbon.2013.07.063).
22. 22)
  - 26. Graf, D., Molitor, F., Ensslin, K., Stampfer, C., Jungen, A., Hierold, C., Wirtz, L.: ‘Spatially resolved Raman spectroscopy of single-and few-layer graphene’, Nano Lett., 2007, 7, (2), pp. 238–242 (doi: 10.1021/nl061702a).
23. 23)
  - C. Berger , Z. Song , T. Li . Ultrathin epitaxial graphite: 2D electron gas properties and a route toward graphene-based nanoelectronics. J. Phys. Chem. B , 52 , 19912 - 19916

Numerous single-layer graphene sheets prepared from natural graphite by non-chemical liquid-phase exfoliation

References

Related content