Er3+-doped multicomponent glass core fibre amplifier pumped at 1.48 μm

Er3+-doped multicomponent glass core fibre amplifier pumped at 1.48 μm

For access to this article, please select a purchase option:

Buy article PDF
£12.50
(plus tax if applicable)
Buy Knowledge Pack
10 articles for £75.00
(plus taxes if applicable)

IET members benefit from discounts to all IET publications and free access to E&T Magazine. If you are an IET member, log in to your account and the discounts will automatically be applied.

Learn more about IET membership 

Recommend to library

You must fill out fields marked with: *

Librarian details
Name:*
Email:*
Your details
Name:*
Email:*
Department:*
Why are you recommending this title?
Select reason:
 
 
 
 
 
Electronics Letters — Recommend this title to your library

Thank you

Your recommendation has been sent to your librarian.

An excellent fibre amplifier of Er3+-doped silica fibre with a multicomponent core composed of Na2O, CaO, Al2O3, SiO2, and Er3+, is realised. A maximum signal gain of 37 dB for a pump power of 23 mW at 1.48 μm and the gain coefficient of 3.5 dB/mW are attained.

References

    1. 1)
      • Saito, S., Imai, T., Sugie, T., Ohkawa, N., Ichihashi, Y., Ito, T.: `An over 2,200 km coherent transmission experiment at 2.5 Gbit/s using erbium-doped fibre amplifiers', Postdeadline pap. PD2-1, Tech. Dig. Opt. Fiber Commun. Conf., 1990, San Francisco.
    2. 2)
      • C.G. Atkins , J.F. Massicott , J.R. Armitage , R. Wyatt , B.J. Ainslie , S.P. Craig-Ryan . High-gain, broad spectral bandwidth erbium-doped fibre amplifier pumped near 1.5 μm. Electron. Lett. , 910 - 911
    3. 3)
      • Miller, C.A., Brierley, M.C., France, P.W.: `Optical amplification in an erbium-doped fluorozirconate fibre between 1480 nm and 1600 nm', ECOC '88, 1988, p. 66–69, part 1.
    4. 4)
      • E. Snitzer , R. Tumminelli . SiO2-clad fibres with selectively volatilized soft glass cores. Opt. Lett. , 757 - 759
    5. 5)
      • M. Yamada , M. Shimizu , M. Horiguchi , M. Okayasu , E. Sugita . Gain characteristics of an Er3+-doped multicomponent glass single-mode optical fibre. IEEE Photonics Technol. Lett. , 656 - 658
    6. 6)
      • M.E. Lines , J.B. MacChesney , K.B. Lyons , A.J. Bruce , A.E. Miller , K. Nassau . Calcium aluminate glasses as potential ultralow-loss optical material at 1.5–1.9 μm. J. Non-Cryst. Solids , 251 - 260
    7. 7)
      • Saifi, M.A., Andrejco, M.J., Way, W.I., von Lehman, A., Yi-Yan, A., Chinlon Lin, , Bilodeau, F., Hill, K.O.: `Er', FA6, OFC '91, 1991.
http://iet.metastore.ingenta.com/content/journals/10.1049/el_19911327
Loading

Related content

content/journals/10.1049/el_19911327
pub_keyword,iet_inspecKeyword,pub_concept
6
6
Loading
This is a required field
Please enter a valid email address