Er3+-doped multicomponent glass core fibre amplifier pumped at 1.48 μm

Er3+-doped multicomponent glass core fibre amplifier pumped at 1.48 μm

For access to this article, please select a purchase option:

Buy article PDF
£12.50
(plus tax if applicable)
Buy Knowledge Pack
10 articles for £75.00
(plus taxes if applicable)

IET members benefit from discounts to all IET publications and free access to E&T Magazine. If you are an IET member, log in to your account and the discounts will automatically be applied.

Learn more about IET membership 

Recommend Title Publication to library

You must fill out fields marked with: *

Librarian details
Name:*
Email:*
Your details
Name:*
Email:*
Department:*
Why are you recommending this title?
Select reason:
 
 
 
 
 
Electronics Letters — Recommend this title to your library

Thank you

Your recommendation has been sent to your librarian.

An excellent fibre amplifier of Er3+-doped silica fibre with a multicomponent core composed of Na2O, CaO, Al2O3, SiO2, and Er3+, is realised. A maximum signal gain of 37 dB for a pump power of 23 mW at 1.48 μm and the gain coefficient of 3.5 dB/mW are attained.

References

    1. 1)
      • Miller, C.A., Brierley, M.C., France, P.W.: `Optical amplification in an erbium-doped fluorozirconate fibre between 1480 nm and 1600 nm', ECOC '88, 1988, p. 66–69, part 1.
    2. 2)
      • C.G. Atkins , J.F. Massicott , J.R. Armitage , R. Wyatt , B.J. Ainslie , S.P. Craig-Ryan . High-gain, broad spectral bandwidth erbium-doped fibre amplifier pumped near 1.5 μm. Electron. Lett. , 910 - 911
    3. 3)
      • Saito, S., Imai, T., Sugie, T., Ohkawa, N., Ichihashi, Y., Ito, T.: `An over 2,200 km coherent transmission experiment at 2.5 Gbit/s using erbium-doped fibre amplifiers', Postdeadline pap. PD2-1, Tech. Dig. Opt. Fiber Commun. Conf., 1990, San Francisco.
    4. 4)
      • M. Yamada , M. Shimizu , M. Horiguchi , M. Okayasu , E. Sugita . Gain characteristics of an Er3+-doped multicomponent glass single-mode optical fibre. IEEE Photonics Technol. Lett. , 656 - 658
    5. 5)
      • Saifi, M.A., Andrejco, M.J., Way, W.I., von Lehman, A., Yi-Yan, A., Chinlon Lin, , Bilodeau, F., Hill, K.O.: `Er', FA6, OFC '91, 1991.
    6. 6)
      • E. Snitzer , R. Tumminelli . SiO2-clad fibres with selectively volatilized soft glass cores. Opt. Lett. , 757 - 759
    7. 7)
      • M.E. Lines , J.B. MacChesney , K.B. Lyons , A.J. Bruce , A.E. Miller , K. Nassau . Calcium aluminate glasses as potential ultralow-loss optical material at 1.5–1.9 μm. J. Non-Cryst. Solids , 251 - 260
http://iet.metastore.ingenta.com/content/journals/10.1049/el_19911327
Loading

Related content

content/journals/10.1049/el_19911327
pub_keyword,iet_inspecKeyword,pub_concept
6
6
Loading
This is a required field
Please enter a valid email address